Liquid Marine Orthophthalic Unsaturated Polyester Resin
Basic Info.
Product Description
Product details
Model
|
Type
|
25ºC pa.s
Viscosity |
Min Gel Time
|
Non-volatile
|
MPa
Tensile Strength |
Elongation
|
MPa Flexural Strength
|
HDT ºC
|
191DC-G
|
DC
|
0.20-0.45
|
6.0-12.0
|
68-74
|
58
|
2.9
|
93
|
85
|
DC191
|
DC
|
0.20-0.45
|
6.0-12.0
|
68-74
|
58
|
2.9
|
93
|
85
|
191
|
PA
|
0.25-0.45
|
9.0-17.0
|
61-70
|
60
|
3.5
|
112
|
70
|
9196
|
DC
|
0.25-0.45
|
5.0-18.0
|
68-75
|
50
|
2
|
90
|
85
|
196
|
PA
|
0.25-0.45
|
9.0-17.0
|
61-67
|
60
|
1.8
|
113
|
66
|
196F
|
PA
|
0.25-0.45
|
9.0-17.0
|
61-67
|
60
|
1.8
|
111
|
66
|
5118F
|
ISPA
|
0.35-0.80
|
5.0-13.0
|
63-71
|
60
|
2.3
|
110
|
70
|
199
|
ISPA
|
0.35-0.65
|
10.0-16.0
|
56-64
|
55
|
1.8
|
90
|
120
|
199X
|
PA
|
0.35-0.65
|
13.0-19.0
|
56-62
|
60
|
2
|
90
|
115
|
3301
|
ABPA
|
0.35-0.58
|
5.8-10.7
|
56-62
|
55
|
2
|
105
|
100
|
197
|
ABPA
|
0.40~0.50
|
10~25
|
47~53
|
60
|
2
|
90
|
115
|
Product description
Item
|
Range
|
unit
|
Testing method
|
appearance
|
Light yellow viscous liquid
|
–
|
GB/T 8237.4.1.1
|
Acid value
|
25-30
|
mgKOH/g
|
GB/T 2895
|
Viscosity,25ºC
|
0.25-0.45
|
Pa.s
|
GB/T 7193.1
|
Solid content
|
61-70
|
%
|
GB/T 7193.3
|
Gel time ,25ºC
|
9-17
|
min
|
GB/T 7193-2008
|
Item
|
Unit
|
Measured value
|
Testing method
|
Barco hardness
|
—
|
41
|
GB 3854-83
|
Heat distortion temperature
|
ºC
|
70
|
GB 1634-04
|
Bending strength
|
MPa
|
112
|
GB/T 2570-95
|
Tensile Strength
|
MPa
|
60
|
GB/T 2568-95
|
Elongation at break
|
%
|
3.5
|
GB/T 2568-95
|
Impact strength
|
KJ/m2
|
10.2
|
GB/T 2571-95
|
1.Casting body preparation method according to GB8237-87
2.Curing system: hardener 55%MEKP:2% , promoter E1:2% post cure system: 60ºC×2h + 80ºC×2h
Item
|
Unit
|
Measured data
|
Testing method
|
Bending strength
|
MPa
|
365
|
GB/T1449-83
|
Tensile Strength
|
MPa
|
290
|
GB/T1447-83
|
1.casting body preparation method according to GB8237-87
2.Curing system: hardener 55%MEKP:2% , promoter E1:2% post cure system: 60ºC×3h + 110ºC×3h
Liquid resin package and storage conditions
-Try to prevent liquid resin from directly sunshine and heat resource
-Prohibit open before use
-Flammable, should keep away from open fire
-Shelf life is 6 month under 25ºC
-Store and operate in a dry, well-ventilated place
-Please read MSDS carefully before use this product
Application
Our Factory
We are China Liquid Marine Orthophthalic Unsaturated Polyester Resin manufacture and supplier,You can get more details with Email,you will get cheap price or factory price.
Get Latest Price Request a quote
Popular kesswil Products
Recycled HDPE Pellets Pipe Grade HDPE Granules for PE 100 Pipes
China Supplier Cathode Copper Sheet
Plastic Raw Material Film Grade LDPE Pellet Virgin for Pipe Packaging
High Quality Food Additive Citric Acid Anhydrate
12-40 Mesh Monohydrate Citric Acid for Food Industry
Recycled Pet Resin Pellets Chips for Pet RPET Filament Yarn
Popular Liquid Marine Orthophthalic Unsaturated Polyester Resin Products
Popular Polyester Products
Fiberglass Unsaturated Polyester Resin Boat Building
Unsaturated Polyester Resin for Resin Arts and Crafts
Resin Polyester Resin for Fiberglass Boats Spraying Hand Pasting
Liquid Fiberglass Unsaturated Polyester Resin for FRP Pipes and Tank
Polyester Polyol/Polyester Polyol Plant/Polyester Polyol Resin
Tags: kesswil, Liquid Marine Orthophthalic Unsaturated Polyester Resin, Polyester, Polyester Resin