Fiberglass Unsaturated Polyester Resin Boat Building Epoxy Resin for Boat
Basic Info.
Product Description
Product details
Model
|
Type
|
25ºC pa.s
Viscosity |
Min Gel Time
|
Non-volatile
|
MPa
Tensile Strength |
Elongation
|
MPa Flexural Strength
|
HDT ºC
|
191DC-G
|
DC
|
0.20-0.45
|
6.0-12.0
|
68-74
|
58
|
2.9
|
93
|
85
|
DC191
|
DC
|
0.20-0.45
|
6.0-12.0
|
68-74
|
58
|
2.9
|
93
|
85
|
191
|
PA
|
0.25-0.45
|
9.0-17.0
|
61-70
|
60
|
3.5
|
112
|
70
|
9196
|
DC
|
0.25-0.45
|
5.0-18.0
|
68-75
|
50
|
2
|
90
|
85
|
196
|
PA
|
0.25-0.45
|
9.0-17.0
|
61-67
|
60
|
1.8
|
113
|
66
|
196F
|
PA
|
0.25-0.45
|
9.0-17.0
|
61-67
|
60
|
1.8
|
111
|
66
|
5118F
|
ISPA
|
0.35-0.80
|
5.0-13.0
|
63-71
|
60
|
2.3
|
110
|
70
|
199
|
ISPA
|
0.35-0.65
|
10.0-16.0
|
56-64
|
55
|
1.8
|
90
|
120
|
199X
|
PA
|
0.35-0.65
|
13.0-19.0
|
56-62
|
60
|
2
|
90
|
115
|
3301
|
ABPA
|
0.35-0.58
|
5.8-10.7
|
56-62
|
55
|
2
|
105
|
100
|
197
|
ABPA
|
0.40~0.50
|
10~25
|
47~53
|
60
|
2
|
90
|
115
|
Product description
Item
|
Range
|
unit
|
Testing method
|
appearance
|
Light yellow viscous liquid
|
–
|
GB/T 8237.4.1.1
|
Acid value
|
25-30
|
mgKOH/g
|
GB/T 2895
|
Viscosity,25ºC
|
0.25-0.45
|
Pa.s
|
GB/T 7193.1
|
Solid content
|
61-70
|
%
|
GB/T 7193.3
|
Gel time ,25ºC
|
9-17
|
min
|
GB/T 7193-2008
|
Item
|
Unit
|
Measured value
|
Testing method
|
Barco hardness
|
—
|
41
|
GB 3854-83
|
Heat distortion temperature
|
ºC
|
70
|
GB 1634-04
|
Bending strength
|
MPa
|
112
|
GB/T 2570-95
|
Tensile Strength
|
MPa
|
60
|
GB/T 2568-95
|
Elongation at break
|
%
|
3.5
|
GB/T 2568-95
|
Impact strength
|
KJ/m2
|
10.2
|
GB/T 2571-95
|
1.Casting body preparation method according to GB8237-87
2.Curing system: hardener 55%MEKP:2% , promoter E1:2% post cure system: 60ºC×2h + 80ºC×2h
Item
|
Unit
|
Measured data
|
Testing method
|
Bending strength
|
MPa
|
365
|
GB/T1449-83
|
Tensile Strength
|
MPa
|
290
|
GB/T1447-83
|
1.casting body preparation method according to GB8237-87
2.Curing system: hardener 55%MEKP:2% , promoter E1:2% post cure system: 60ºC×3h + 110ºC×3h
Liquid resin package and storage conditions
-Try to prevent liquid resin from directly sunshine and heat resource
-Prohibit open before use
-Flammable, should keep away from open fire
-Shelf life is 6 month under 25ºC
-Store and operate in a dry, well-ventilated place
-Please read MSDS carefully before use this product
Application
Our Factory
We are China Fiberglass Unsaturated Polyester Resin Boat Building Epoxy Resin for Boat manufacture and supplier,You can get more details with Email,you will get cheap price or factory price.
Get Latest Price Request a quote
Popular Fiberglass Unsaturated Polyester Resin Boat Building Epoxy Resin for Boat Products
Popular kesswil Products
Food Grade Monohydrate Anhydrous Monohydrate Citric Acid Powder
Upe Rod Ultra High Molecular Weight Polyethylene Rod
Low Price Colorless Solution H3po4 Tech Grade/Food Grade
Industry Grade Chrome Oxide Green 99% Made by Chromic Acid
Quality Copper Wire 99.95%-99.99%Copper Wire Scrap
Factory Customized Pure Aluminum Aluminum Alloy
Popular Polyester Products
Food Additives Citric Acid Monohydrate/Citric Acid
Polyester Resin for Fiberglass Boats Hand Made Type Ortho Resin
Unsaturated Polyester Resin for Resin Arts and Crafts
Ksw Multipurpose Unsaturated Fibre Glass Boat Casting Resin Unsaturated Polyester Resin
Liquid Fiberglass Unsaturated Polyester Resin for FRP Pipes and Tank
Tags: Fiberglass Unsaturated Polyester Resin Boat Building Epoxy Resin for Boat, kesswil, Polyester, Polyester Resin